Shibaam Nylon Rods, Bushes, Profiles, and Machinery parts are characterized by a combination of high strength, toughness and abrasion resistances. Nylon products replace metals in various engineering applications as they have excellent physical and mechanical properties.
PA sheets and rods are thermoplastics extruded from polyamide(Nylon) PA6. It has high mechanical strength, wear resistance, easy processing, good creep resistance and mechanical shock absorption. The service temperature is-40°C 110°C.
Standard Sizes
Sheet: Thickness X Width x Length
6-150mm x 1000mm X 2000mm
Rod: diameter x length
16-400mm X 1000mm
Customised sizes can be made to order
Strengthening gears, bearings, and more, PA6 supports engineering with its robustness and resilience.
PA6 keeps machines running smoothly, ensuring efficient and reliable manufacturing processes.
In industrial settings like paper and sugar mills, PA6 maintains operations with its durability and reliability.
PA6 stands strong in railways, enhancing safety and reliability in critical components.
From conveyors to rollers, PA6's durability improves material handling equipment performance.
PA6 components uphold standards in bottling and food processing, ensuring hygienic and efficient processes.
Across industries, PA6 excels in processing applications, demonstrating adaptability and dependability.
Automotive engine parts benefit from PA6's strength and resilience, boosting overall performance.
| Performance and Test Conditiom | Test Method | Unit | Tyical Values |
| Notched impact strength of cantilever beam, 23°C | ASTM D256 | KJ/m² | 8 |
| Yield tensile strength, 23°C, 50mm/min | ASTM D638 | Mpa | 75 |
| Elongation at break, 23°C, 50mm/min | ASTM D638 | % | 5 |
| The bending strength. 23C, 2mm/min | ASTM 790 | Mpa | 90 |
| Bending modulus, 23°C, 2mm/min | ASTM 790 | Mpa | 2200 |
| Shore hardness D | ASTMD2240 | – | 80 |
| The Density | ISO 1183 | g/cm3 | 1.13 |
| Performance and Test Conditiom | Test Method | Unit | Tyical Values |
| Thermal deformation temprature(HDT) (0.45Mpa) | ISO 75 | °C | 70 |
| Melting point | – | °C | 220 |
| Long term operating temperature | – | °C | 80 |
| Short-term operating temperature | – | °C | 110 |
| Thermal conductivity | DIN 52612-1 | W/(K-M) | 0.23 |
| Linear expansion coefficient | ASTM D696 | 10-5-1/K | 8 |
| Performance and Test Conditiom | Test Method | Unit | Tyical Values |
| Dielectric strength | ASTM D150 | KV-mm | 25 |
| Dielectric loss coefficient | ASTM D150 | – | 0.032 |
| The volume resistance | ASTM D257 | Ω.cm | 1015 |
| The surface resistance | ASTM D257 | Ω | 1015 |
| Dielectric constant | ASTM D149 | – | 4.2 |